![]() ![]() The second section, thermal soak, is typically a 60 to 120 second exposure for removal of solder paste volatiles and activation of the fluxes (see flux), where the flux components begin oxidereduction on component leads and pads. The preheat section is where the solvent in the paste begins to evaporate, and if the rise rate (or temperature level) is too low, evaporation of flux volatiles is incomplete. Solder paste can also have a spattering effect. If the rate exceeds the maximum slope, damage to components from thermal shock or cracking can occur. The ramp–up rate is usually somewhere between 1.0 ☌ and 3.0 ☌ per second, often falling between 2.0 ☌ and 3.0 ☌ (4 ☏ to 5 ☏) per second. The preheat zone is often the lengthiest of the zones and often establishes the ramp-rate. Maximum slope is a temperature/time relationship that measures how fast the temperature on the printed circuit board changes. In the conventional reflow soldering process, there are usually four stages, called "zones", each having a distinct thermal profile: preheat, thermal soak (often shortened to just soak), reflow, and cooling. The goal of the reflow process is to melt the solder and heat the adjoining surfaces, without overheating and damaging the electrical components. When used on boards containing a mix of SMT and THT components, through-hole reflow allows the wave soldering step to be eliminated from the assembly process, potentially reducing assembly costs. Because wave soldering can be simpler and cheaper, reflow is not generally used on pure through-hole boards. Reflow soldering is the most common method of attaching surface mount components to a circuit board, although it can also be used for through-hole components by filling the holes with solder paste and inserting the component leads through the paste. Heating may be accomplished by passing the assembly through a reflow oven or under an infrared lamp or by soldering individual joints with a hot air pencil. Reflow soldering is a process in which a solder paste (a sticky mixture of powdered solder and flux) is used to temporarily attach one or several electrical components to their contact pads, after which the entire assembly is subjected to controlled heat, which melts the solder, permanently connecting the joint. Shenzhen Jaguar Automation Equipment Co., Ltd Reflow soldering process-Technical Data-Shenzhen Jaguar Automation Equipment Co., Ltd-reflow oven wave soldering machine manufacturer ![]()
0 Comments
Leave a Reply. |
AuthorWrite something about yourself. No need to be fancy, just an overview. ArchivesCategories |